辐照交联低烟无卤阻燃聚烯烃护套料 FEHW90, FEHW105, FEHW125, FEHW150
Irradiation Cross-linkable Low-smoke Halogen-free Flame-retardant Polyolefin Jacketing Compound ...
型号:0

参考价:¥

说明:如您对该产品感兴趣,请在此输入您的手机号将本产品的地址 发送至您手机上。
Description and Application 产品描述和用途
FEHW90, FEHW105, FEHW125, FEHW150 are irradiation cross-linkable low-smoke halogen-free jacketing compounds, which don’t contain heavy metals like Pb, Ba, Cd, Cr, Sn and Sb. Their properties can well meet RoHS Standard. They have good physical and mechanical properties, especially good temperature-resistant performances. They are mainly used for the jacketing of communication cables, control cables and power cable.
FEHW90,FEHW105,FEHW125,FEHW150是可辐照交联低烟无卤护套料。不含Pb、Ba、Cd、Cr、Sn、Sb六大重金属。满足RoHS标准要求。产品具有良好的物理机械性能,尤其是较好的耐温性。主要用于通信电缆,控制电缆和电力电缆的护套层。
 
Processing Indicator   加工工艺
Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
采用低烟无卤专用螺杆,长径比L/D=20-25。
Model
牌号
Machine Barrel Temperature
机筒温度
Molding Temprature
机头温度
FEHW90/FEHW105/FEHW125/
FEHW150
130-140℃
150-160℃
 
 
Physical and Electrical Properties 物理及电性能指标
Item
试验项目
Unit
单位
Specification
技术要求
FEHW90
FEHW105
FEHW125
FEHW150
Tensile Strength
拉伸强度
MPa
≥10
≥10
≥10
≥10
Elongation at Break
断裂伸长率
%
≥150
≥150
≥150
≥150
Density
密度
g/cm3
≤1.5
≤1.5
≤1.45
≤1.45
Dielectric Strength
介电强度
MV/m
≥20
≥20
≥20
≥20
Aging Conditions
热老化条件
/
121℃×168h
136℃×168h
158℃×168h
180℃×168h
Tensile Strength Variation
 After Aging
老化后拉伸强度变化率
%
≥75
≥75
≥75
≥75
Elongation Variation After Aging
老化后断裂伸长率变化率
%
≥75
≥75
≥75
≥75
Brittle Temperature With Low Temperature Impact
冲击脆化温度
-40
-40
-40
-40
Volume Resistivity at 20℃
20℃体积电阻率
Ω·m
≥1.0×1011
≥1.0×1011
≥1.0×1011
≥1.0×1011
Hot Set Test Condition
热延伸试验条件
200℃×0.2MPa×15min
Hot Elongation
负荷下伸长率
%
≤100
≤100
≤100
≤100
Set
冷却后永久形变
%
≤15
≤15
≤15
≤15
Water Absorption
吸水性实验
14 days at 70℃
mg/cm2
≤5
≤5
≤5
≤5
Oxygen Index
氧指数
%
≥32
≥32
≥32
≥28
HCLGas Evolution
HCL气体发生量
Mg/g
≤1.0
≤1.0
≤1.0
≤1.0
PH Value
PH值
/
≥4.3
≥4.3
≥4.3
≥4.3
Smoke Density烟密度
– No-flame Mode无焰模式
– Flame Mode有焰模式
Ds max
 
≤250
≤100
 
≤250
≤100
 
≤250
≤100
 
≤250
≤100
Conductivity
电导率
uS/mm
≤10
≤10
≤10
≤10
Toxicity Index
毒性
/
≤5.0
≤5.0
≤5.0
≤5.0
 
Suggestedirradiation dose:12-15 mega-tera.建议的辐照剂量为:12-15兆拉。
 

Attentions 注意事项:
1)The compound should be dried before using if the package is broken. Once package is open, recommend to run out within 12 hours.
原料破包需烘干后才能使用,材料一经开封,建议12小时之内用完。
2)Please ensure the screw, barrel, hopper are thoroughly cleaned before operation. Avoid bringing impurities while processing.
加工前确保螺杆、机筒、加料斗彻底清理干净,加工过程中严禁带入杂质。
3)If you need a faster extrusion. Please accelerate screw speed gradually to avoid inadequate plasticizing which may cause rough surface of the cables.
如果要快速挤出时,请慢慢逐渐加快螺杆转速,以免塑化不良,电缆表面毛糙。